TMT Bars

Manufacturing process

TMT Bar

Requirement of High Strength Rebars Problems associated with High Strength Rebars Technological developments in production processes of High Strength Rebars
Comparison of different processes for production of High Strength Rebars TMT Bars Manufacturing process TMT bars vs “Quenched & Tempered” bars
Advantages & Applications International Scenario Indian Scenario

TMT Bars manufacturing process

Under thermo mechanical treatment, the steel bars are passed through a specially designed water-cooling system where they are kept till the outer surface of the bars becomes colder while the core remains hot. This creates a temperature gradient in the bars.

After the intensive cooling, the bar is exposed to air and the core re-heats the quenched surface layer by conduction, therefore tempering the external martensite.

When the bars are taken out of the cooling system, the heat flows from the core to the outer surface, further tempering of the bars, which helps them attain a higher yield strength. The resulting heat-treated structure imparts superior strength and toughness to the bars.

Cooling process is illustrated below:
TMT Cooling process graph
The pre-determined cooling of the bar periphery transforms the peripheral structure to martensite and then annealed through the heat available at the core.

The peripheral and core temperature difference finally equalises at around 600 0C and the resultant bar structure is of tempered martensite at the periphery and of fine-grained ferrite-pearlite at the core.

Generally speaking, the resultant soft core forms about 65-75 per cent of the area (depending upon the desired minimum yield strength) and the rest is the hardened periphery.

The equalizing temperature together with the final rolling temperature is the most important parameter to achieve the required mechanical properties.

Finally, when the bar is discharged on to the Cooling Beds, the remaining austenite transforms into a very fine-grained pearlite structure.

The figure below illustrates a typical TMT bar manufacturing process:

TMT Manufacturing process

After this process of thermo mechanical treatment, a dark etched peripheral rim of tempered martensite and a grey core of ferrite pearlite get formed.

The tempered martensite surface layer is very hard while the microstructure of the core is a very fine-grained ferrite and pearlite which is quite soft. The result is a structure with a high yield strength combined with high ductility.

TMT microstructure

TMT microstructure Microstructure of TMT bar showing peripheral rim of tempered martensite & core of ferrite pearlite get formed TMT microstructure
Tempered Martensite Rim

TMT microstructureFerrite-Pearlite core

TMT bars are also known as ‘Quenched and Tempered rebars’, because of the quenching and tempering processes involved in making the bars.

The production of quality TMT bar depends on three major factors :

    • Quality of raw materials
    • A properly designed and automated mill; and
    • A well-designed quenching and tempering technology

 

TMT bars having uniform and concentrated hardened periphery and the softer core will have the desired tensile strengths coupled with high elongation as required in seismic zones.

Depending on the size and grade, rebars with hardened periphery of about 15 to 30 per cent of the cross sectional area of the bar are ideal for civil constructions (constructions of houses, offices, etc.)

*****

References:
Latest developments on steel front” by Jagvir Goyal
Thermex Quenching and Tempering Technology” by R.K. Markan, the Chairman and Managing Director of H&K India
Websites of SAIL, Rajuri steel & Evcon